FeCrAl 0cr23al5 singa fanafanana tariby fisaka &esoryavy amin'ny orinasa
kilasy | 0Cr23Al5 |
Size | hateviny: 0.05-3mm sakany: 4-250mm |
Surface | mamirapiratra slitting |
lanja | 1-3kg / horonana, araka ny habetsahan'ny mpanjifa |
Resistivity | 1.3±0.05μΩ.m |
Hardness (HV) | 180-210HV |
Elongation | ≥16% |
kilasy | Temperature ambony indrindra | Resistivity | hamafin'ny | Faharetana amin'ny sintona | Elongation |
0Cr13Al4 | 1050 ℃ | 1,25±0,05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
0Cr15Al5 | 1100 ℃ | 1.3±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
0Cr21Al6Nb | 1300 ℃ | 1,42±0,05μΩ.m | 200-240HV | 750N/mm2 | ≥12 |
Cr20Ni80 | 1200 ℃ | 1,09±0,05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
Cr15Ni60 | 1150 ℃ | 1,12±0,05μΩ.m | 175-210HV | 750N/mm2 | ≥20 |
Cr20Ni35 | 1100 ℃ | 1,04±0,05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
Cr25Ni20(310S) | 1100 ℃ | 0,86±0,05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
kilasy | Famoronana simika% | ||||||||
C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
≤ | |||||||||
0Cr15Al5 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | <1 | 4.8-5.0 | Mila mahay mandanjalanja |
0Cr21Al6Nb | 0.05 | 0.025 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | Mila mahay mandanjalanja |
0Cr13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | <1 | 4.8-5.0 | Mila mahay mandanjalanja |
Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | Mila mahay mandanjalanja | <0.5 | ≤1.0 |
Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | <0.5 | Mila mahay mandanjalanja |
Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | Mila mahay mandanjalanja |
Cr25Ni20 | 0.08 | 0.045 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | - | Mila mahay mandanjalanja |
Shanghai Tankii ALloy Material Co., Ltd.mifantoka amin'ny famokarana ny nichrome firaka, thermocouple tariby, fecral firaka, mazava tsara firaka, varahina nikela firaka, mafana spray firaka sns amin'ny endrika tariby, taratasy, kasety,esory, tsorakazo sy takelaka.
Efa nahazo mari-pankasitrahana rafitra kalitao ISO 9001 izahay ary fankatoavana ny rafitra fiarovana ny tontolo iainana ISO 14001. Manana andiana famokarana mandroso feno amin'ny fanadiovana, fampihenana mangatsiaka, sary ary fitsaboana hafanana sns izahay. Manana fahaiza-manao R&D mahaleo tena ihany koa izahay.